Adhesion Energy in the Metal/Oxide System for the Case of High-Temperature Oxidation of Nickel-Based Superalloys

Тип публикации: статья из журнала

Год издания: 2017

Идентификатор DOI: 10.1134/S0036029517100135

Ключевые слова: nickel-based superalloy, high-temperature oxidation, oxide layer, microstructure, adhesion energy

Аннотация: The microstructure of the oxide layer is studied and the adhesion energy of the metal/oxide interface is determined after high-temperature isothermal oxidation (T = 1150 degrees C) of a single-crystal commercial Rene N5 nickel alloy. Experiments upon heating and rapid cooling are performed to initiate failure of the oxide layer. The elastic energy of the metal/oxide interface is determined using the model of circular buckling followed by edge delamination. Calculations are conducted for a homogeneous alumina layer and with allowance for the multilayer structure that forms at the initial stages of alloy oxidation. The adhesion energy is 72 and 27 J/m(2) for these cases, respectively.

Ссылки на полный текст

Издание

Журнал: RUSSIAN METALLURGY

Выпуск журнала: Is. 10

Номера страниц: 884-889

ISSN журнала: 00360295

Место издания: MOSCOW

Издатель: PLEIADES PUBLISHING INC

Авторы

  • Moskvichev V.V. (SB RAS, Inst Computat Technol, Krasnoyarsk Branch Off, Krasnoyarsk 660049, Russia)
  • Sukhodoeva N.V. (Siberian Fed Univ, Krasnoyarsk 660041, Russia)
  • Fedorova E.N. (SB RAS, Inst Computat Technol, Krasnoyarsk Branch Off, Krasnoyarsk 660049, Russia; Siberian Fed Univ, Krasnoyarsk 660041, Russia)
  • Popov A.S. (Siberian Fed Univ, Krasnoyarsk 660041, Russia)

Вхождение в базы данных

Информация о публикациях загружается с сайта службы поддержки публикационной активности СФУ. Сообщите, если заметили неточности.

Вы можете отметить интересные фрагменты текста, которые будут доступны по уникальной ссылке в адресной строке браузера.