Тип публикации: статья из журнала
Год издания: 2017
Идентификатор DOI: 10.1088/1612-202X/aa7603
Ключевые слова: laser materials, molybdate crystals, Raman spectra, stimulated-emission, ytterbium
Аннотация: Crystal with composition Li2Zn2(MoO4)3 doped with 0.7 at.% Yb (Yb:LiZnMo), with high optical quality and a length of a few cm is grown from the flux using Li2MoO4 as a solvent. Yb:LiZnMo is orthorombic (sp. gr. Pnma, a = 5.0843 Å, b = 10.4927 Å, c = 17.6742 Å, Z = 4). Polarized Raman spectra are studied for this crystal; the most intense band is observed at 898 cm-1. The absorption, stimulated-emission and gain cross-sections of Yb3+ ions are determined for the principal light polarizations, E || a, b, c. The maximum σ SE = 6.6 × 10-21 cm2 at 1011 nm for E || b. The gain bandwidth for Yb:LiZnMo is up to ∼50 nm. The radiative lifetime of the Yb3+ ions is 1.55 ms. The Yb:LiZnMo crystals are very promising for broadly tunable lasers. © 2017 Astro Ltd.
Издание
Журнал: Laser Physics Letters
Выпуск журнала: Vol. 14, Is. 8
Номера страниц: 85804
ISSN журнала: 16122011
Издатель: Institute of Physics Publishing
Персоны
- Kurilchik S. (Center for Optical Materials and Technologies (COMT), Belarusian National Technical University, 65/17 Nezavisimosti Ave., Minsk, Belarus, Kazan Federal University, 18 Kremlevskaya St., Kazan, Russian Federation)
- Loiko P. (ITMO University, 49 Kronverkskiy pr., St. Petersburg, Russian Federation)
- Yasukevich A. (Center for Optical Materials and Technologies (COMT), Belarusian National Technical University, 65/17 Nezavisimosti Ave., Minsk, Belarus)
- Trifonov V. (A.V. Nikolaev Institute of Inorganic Chemistry, Siberian Branch of Russian Academy of Sciences, 3 Lavrentyev Ave., Novosibirsk, Russian Federation)
- Volokitina A. (ITMO University, 49 Kronverkskiy pr., St. Petersburg, Russian Federation)
- Vilejshikova E. (Center for Optical Materials and Technologies (COMT), Belarusian National Technical University, 65/17 Nezavisimosti Ave., Minsk, Belarus)
- Kisel V. (Center for Optical Materials and Technologies (COMT), Belarusian National Technical University, 65/17 Nezavisimosti Ave., Minsk, Belarus)
- Mateos X. (Física i Cristal lografia de Materials i Nanomaterials (FiCMA-FiCNA), Universitat Rovira i Virgili (URV), Campus Sescelades, c/ Marcel•lí Domingo, s/n., Tarragona, Spain)
- Baranov A. (ITMO University, 49 Kronverkskiy pr., St. Petersburg, Russian Federation)
- Goriev O. (Kazan Federal University, 18 Kremlevskaya St., Kazan, Russian Federation)
- Kuleshov N. (Center for Optical Materials and Technologies (COMT), Belarusian National Technical University, 65/17 Nezavisimosti Ave., Minsk, Belarus)
- Pavlyuk A. (A.V. Nikolaev Institute of Inorganic Chemistry, Siberian Branch of Russian Academy of Sciences, 3 Lavrentyev Ave., Novosibirsk, Russian Federation)
Вхождение в базы данных
Информация о публикациях загружается с сайта службы поддержки публикационной активности СФУ. Сообщите, если заметили неточности.