Аннотация: CsFe(MoO4)2 single crystals have been grown by solution-melt crystallization with a charge-to-solvent ratio of 1 : 3 (with Cs2Mo3O10 used as a solvent). The crystal structure of this compound has been refined by X-ray diffraction (X8 APEX automatic diffractometer, MoK? radiation, 356 F(hkl), R = 0.0178). The trigonal unit cell has the following parameters: a = b = 5.6051(2) A, c = 8.0118(4) A, V= 217.985(15) A3, Z = 1, ?calc = 3.875 g/cm3, and sp. gr.P3?. The structure is composed of alternating layers of FeO6 octa- hedra (with MoO4 tetrahedra attached by sharing vertices) and CsO12 icosahedra. © Pleiades Publishing, Inc., 2010.
Издание
Журнал: Crystallography Reports
Выпуск журнала: Т. 55, № 4
Номера страниц: 591-593
ISSN журнала: 10637745
Место издания: Москва
Издатель: Pleiades Publishing, Ltd. (Плеадес Паблишинг, Лтд)
Персоны
- Bazarov B.G. (Baikal Institute of Nature Management,Siberian Branch,Russian Academy of Sciences)
- Namsaraeva T.V. (Baikal Institute of Nature Management,Siberian Branch,Russian Academy of Sciences)
- Fedorov K.N. (Baikal Institute of Nature Management,Siberian Branch,Russian Academy of Sciences)
- Bazarova Z.G. (Baikal Institute of Nature Management,Siberian Branch,Russian Academy of Sciences)
- Klevtsova R.F. (Institute of Inorganic Chemistry,Siberian Branch,Russian Academy of Sciences)
- Anshits A.G. (Institute of Inorganic Chemistry,Siberian Branch,Russian Academy of Sciences)
- Glinskaya L.A. (Institute of Inorganic Chemistry,Siberian Branch,Russian Academy of Sciences)
- Vereshchagina T.A. (Institute of Chemistry and Chemical Technology,Siberian Branch,Russian Academy of Sciences)
Вхождение в базы данных
- Ядро РИНЦ (eLIBRARY.RU)
- Список ВАК
Информация о публикациях загружается с сайта службы поддержки публикационной активности СФУ. Сообщите, если заметили неточности.