Synthesis of 6H-SiC single-crystal nanowires in a flow of carbon-silicon high-frequency arc plasma

Тип публикации: статья из журнала

Год издания: 2014

Идентификатор DOI: 10.1134/S106378341410014X

Аннотация: Silicon carbide 6H-SiC nanoparticles and nanowires were obtained in carbon-silicon high-frequency arc plasma plasma in a helium atmosphere at a pressure of 0.1-0.6 MPa. It was shown that 6H-SiC nanowires grow from the arc plasma, as well as from the vapor, according to the known mechanism of vapor-solid condensation on a cold surface covered with single-crystal silicon carbide nuclei. The content of silicon carbide nanowires in the condensate reached 60 wt %. The obtained single-crystal silicon 6H-SiC nanowires had the diameter of 15-18 nm and length of 200-600 nm.

Ссылки на полный текст

Издание

Журнал: PHYSICS OF THE SOLID STATE

Выпуск журнала: Vol. 56, Is. 10

Номера страниц: 2107-2111

ISSN журнала: 10637834

Место издания: NEW YORK

Издатель: MAIK NAUKA/INTERPERIODICA/SPRINGER

Авторы

  • Glushchenko G.A. (Kirensky Institute of Physics, Siberian Branch of the Russian Academy of Sciences)
  • Kolonenko A.L. (Siberian Federal University)
  • Dudnik A.I. (Siberian Federal University)
  • Osipova I.V. (Kirensky Institute of Physics, Siberian Branch of the Russian Academy of Sciences)
  • Vnukova N.G. (Kirensky Institute of Physics, Siberian Branch of the Russian Academy of Sciences)
  • Zharkov S.M. (Siberian Federal University)
  • Churilov G.N. (Siberian Federal University)
  • Leonova T.A. (Siberian Federal University)
  • Nemtsev I.V. (Krasnoyarsk Scientific Center, Siberian Branch of the Russian Academy of Sciences)

Вхождение в базы данных

Информация о публикациях загружается с сайта службы поддержки публикационной активности СФУ. Сообщите, если заметили неточности.

Вы можете отметить интересные фрагменты текста, которые будут доступны по уникальной ссылке в адресной строке браузера.