Тип публикации: статья из журнала
Год издания: 2016
Идентификатор DOI: 10.1080/09507116.2016.1143587
Ключевые слова: Diffusion welding, microstructure, sintering, submicron powders, transition zone, Diffusion, Diffusion coatings, Nickel coatings, Vacuum welding, Welds, High quality, Metallic coating, Microstructure and properties, Nickel powders, Transition zones, Welding temperatures, Welding
Аннотация: Investigations were carried out into the microstructure and properties of diffusion-welded joints produced through a submicron nickel powder layer deposited on the metallic coating at welding temperatures of (0.4–0.7) Tm. The results show that using the submicron powder as an activating layer produces high quality diffusion-welded joints at 850 °C, which is equal to 0.6Tm. © 2016 Informa UK Limited, trading as Taylor & Francis Group.
Издание
Журнал: Welding International
Выпуск журнала: Vol. 30, Is. 9
Номера страниц: 723-726
Персоны
- Mikheev A.A. (The Siberian State Aerospace University named after Academician M. F. Reshetnev)
- Zeer G.M. (Siberian Federal University)
- Koroleva Y.P. (Siberian Federal University)
- Zelenkova E.G. (Siberian Federal University)
- Sartnaeva A.B. (Siberian Federal University)
Вхождение в базы данных
- Scopus
- Ядро РИНЦ (eLIBRARY.RU)
- Список ВАК
Информация о публикациях загружается с сайта службы поддержки публикационной активности СФУ. Сообщите, если заметили неточности.