Peculiarities of Intermetallic Phase Formation in the Process of a Solid State Reaction in (Al/Cu) n Multilayer Thin Films : научное издание | Научно-инновационный портал СФУ

Peculiarities of Intermetallic Phase Formation in the Process of a Solid State Reaction in (Al/Cu) n Multilayer Thin Films : научное издание

Тип публикации: статья из журнала

Год издания: 2021

Идентификатор DOI: 10.1007/s11837-020-04522-9

Аннотация: Phase formation in a solid state reaction in Al/Cu bilayer and multilayer thin films was studied by the methods of in situ transmission electron microscopy, electron diffraction, simultaneous thermal analysis and x-ray diffraction. It was established that the phase formation sequences in the (Al/Cu)n (n = 2, 15) multilayer thin films (θ-Al2Cu → γ1-Al4Cu9 → η2-AlCu) and Al/Cu bilayer thin films (θ-Al2Cu → η2-AlCu → γ1-Al4Cu9) were different. It was assumed that the phase formation process in the thin films was strongly affected by a number of copper/aluminum interfaces due to the changes of aluminum and copper diffusion current.

Ссылки на полный текст

Издание

Журнал: Journal of the Minerals Metals & Materials Society (JOM)

ISSN журнала: 10474838

Издатель: J O M Institute

Авторы

  • Moiseenko E.T. (Siberian Federal University)
  • Zharkov S.M. (Kirensky Institute of Physics,Federal Research Center KSC SB RAS)
  • Altunin R.R. (Siberian Federal University)
  • Belousov O.V. (Institute of Chemistry and Chemical Technology,Federal Research Center KSC SB RAS)
  • Zeer G.M. (Siberian Federal University)
  • Volochaev M.N. (Reshetnev Siberian State University of Science and Technology)
  • Solovyov L.A. (Institute of Chemistry and Chemical Technology,Federal Research Center KSC SB RAS)
  • Yumashev V.V. (Institute of Chemistry and Chemical Technology,Federal Research Center KSC SB RAS)

Вхождение в базы данных

Информация о публикациях загружается с сайта службы поддержки публикационной активности СФУ. Сообщите, если заметили неточности.

Вы можете отметить интересные фрагменты текста, которые будут доступны по уникальной ссылке в адресной строке браузера.