Ключевые слова: aluminum, combined rolling-extruding, electrical resistivity, electromagnetic mold, mechanical properties, rare-earth metals, wire
Аннотация: The article presents the results of studies on the production of wire with a diameter of 0.5 mm from aluminum alloy 01417 with a content of rare-earth metals (REM) in the amount of 7-9% for aircraft construction needs. The deformation modes, the experimental technique and equipment for the implementation of the proposed technology described. The wire was obtained by drawing and bar rolling with subsequent drawing from a rod with a diameter of 5 mm, obtained previously using the process of combined rolling-extruding (CRE) from a continuous ingot with a diameter of 12 mm, cast in an electromagnetic mold (EMM). The wire obtained by the presented technology was subjected to 4 different heat treatment modes with annealing temperatures from 350 to 500 °C and holding time of 1 h in the furnace to achieve mechanical and electrophysical properties corresponding to TS 1-809-1038-2018. The level of strength and plastic properties obtained in the course of research required only one intermediate annealing. The microstructure of the wire was investigated and the modes were revealed that made it possible to obtain the required level of mechanical properties and electrical resistivity, satisfying TS 1-809-1038-2018. © 2020 Trans Tech Publications Ltd, Switzerland.
Журнал: Materials Science Forum
Выпуск журнала: Vol. 992 MSF
Номера страниц: 498-503
ISSN журнала: 02555476
Информация о публикациях загружается с сайта службы поддержки публикационной активности СФУ. Сообщите, если заметили неточности.