Ключевые слова: MCD, Nanoparticles, Ni-C, TEM
Аннотация: Ni-C nanoparticles powder (NP) was synthesized using high-temperature pyrolysis of nickel nitrate in an organic solvent. The NP was characterized by transmission electron microscopy (TEM), energy dispersive x-ray spectroscopy (EDXS) and selected-area electron diffraction (SAED). Structural characterization of the samples confirmed the formation of small, medium and large Ni nanoparticles with face-centered cubic structure (fcc) and enlarged lattice parameter. Magnetic circular dichroism (MCD) of samples with different mean particle sizes showed a red shift with decrease of mean particle size. © Siberian Federal University. All rights reserved.
Издание
Журнал: Journal of Siberian Federal University - Mathematics and Physics
Выпуск журнала: Vol. 9, Is. 4
Номера страниц: 481-484
Персоны
- Petrov Dmitriy A. (Kirensky Institute of Physics SB RAS)
- Ivantsov Ruslan D. (Kirensky Institute of Physics SB RAS)
- Zharkov Sergey M. (Siberian Federal University)
- Lin Chun-Rong (National Pingtung University)
- Shu (National Pingtung University)
- Tseng Yaw-Teng (National Pingtung University)
Вхождение в базы данных
Информация о публикациях загружается с сайта службы поддержки публикационной активности СФУ. Сообщите, если заметили неточности.