Аннотация: ZnS crystals grown form the vapor phase and ZnS/(001)GaAs epitaxial structures grown by metalorganic vapor phase epitaxy are studied by transmission electron microscopy after in situ irradiation in an electron microscope at an electron energy of 400 keV and intensity of (1-4) x 10(19) electrons/cm(2) s. It is shown that irradiation leads to the formation of small (2.5-45 nm) dislocation loops with a density of 1.4 x 10(11) cm(-2), as well as voids and new phase inclusions ae 10 nm in size. Using the moire fringe contrast analysis, these inclusions were identified as ZnO and ZnO2.
Издание
Журнал: PHYSICS OF THE SOLID STATE
Выпуск журнала: Vol. 58, Is. 12
Номера страниц: 2468-2471
ISSN журнала: 10637834
Место издания: NEW YORK
Издатель: MAIK NAUKA/INTERPERIODICA/SPRINGER
Персоны
- Loginov Yu. Yu. (Siberian State Aerosp Univ, Krasnoyarsk 660014, Russia)
- Bril'kov A.V. (Siberian Fed Univ, Krasnoyarsk 660041, Russia)
- Mozzherin A.V. (Siberian Fed Univ, Krasnoyarsk 660041, Russia)
Вхождение в базы данных
Информация о публикациях загружается с сайта службы поддержки публикационной активности СФУ. Сообщите, если заметили неточности.