Synthesis of MnGeO3 polycrystalline and single-crystal samples and comparative analysis of their magnetic properties

Тип публикации: статья из журнала

Год издания: 2009

Идентификатор DOI: 10.1002/pssb.200844013

Аннотация: MnGeO3 single crystals have been grown by a flux method. The obtained MnGeO3 is orthorhombic; a P-bca space group does not undergo any structural phase transitions in the range from room temperature to 900 degrees C. Magnetic measurements carried out for the first time on the MnGeO3 single crystal have revealed higher values (T-N = 38 K and theta = -100 K) as compared to the data for polycrystalline samples reported in the literature (T-N =10 K and 14 K, theta = -54 K and -46 K). These magnetic parameters for polycrystalline samples synthesized by us are close to the literature data. A Mossbauer spectrum taken at T=300 K for a sample containing 5% (Fe2O3)-O-57 shows that manganese ions, Mn2+, occupy two non-equivalent positions and iron is included ina sublattice as Fe2+ and distributed among two positions substituting Mn2+. In this study, the magnetic characteristics are shown to be sensitive even to minor impurity amounts. The MnGeO3 magnetic structure and one of possible reasons causing the effect of impurities on the MnGeO3 magnetic properties are considered in the framework of a simple indirect coupling model. (C) 2009 WILEY-VCH Verlag GmBH & Co. KGaA, Weinheim

Ссылки на полный текст



Выпуск журнала: Vol. 246, Is. 1

Номера страниц: 206-214

ISSN журнала: 03701972

Место издания: MALDEN



Вхождение в базы данных

Информация о публикациях загружается с сайта службы поддержки публикационной активности СФУ. Сообщите, если заметили неточности.

Вы можете отметить интересные фрагменты текста, которые будут доступны по уникальной ссылке в адресной строке браузера.