Anodic process on aluminium bronze in low-temperature cryolite-alumina melts and suspensions

Тип публикации: статья из журнала

Год издания: 2019

Идентификатор DOI: 10.17580/tsm.2019.09.07

Ключевые слова: Alumina, Aluminium, Corrosion, Cryolite melt, Inert anode, Low-temperature electrolysis, Oxidation, Suspensi on

Аннотация: The work is devoted to the anodic behaviour of Cu–Al-based alloys in cryolitealumina melts and suspensions with a cryolite ratio 1.3 and a volume fraction of the dispersed phase in suspensions 0.12 and 0.15 with analytical alumina with average particle size 5 μm. The alloys were investigated by the methods of stationary galvanostatic polarization and cyclic voltammetry. The experiments were carried out at 1023 K. Alloys Cu – 9 Al – 5 Fe (composition A1), Cu – 10 Al (A2) and Cu – 10 Al – 1.7 Be (A3) were used as anodes, the possible oxidation products of the anodes were thermodynamically analyzed, and the standard electrode potentials of the corresponding reactions were calculated. After the experiments, the structure of the oxide layer was investigated. The metal is covered with a dense 0.5–1 mm thick oxides layer. Visible cracks, damage and signs of deep corrosion were not found. The oxide layers of the samples consist mainly of Cu2O and CuAlO2compounds. The transition from the saturated melt to the suspension leads to an increase in the fraction of copper (I) oxide in the oxide layer. The compounds CuO and CuAl2O4are found only in the oxide layers of the anodes of composition A2. Composition A2 and suspensions with the dispersed phase volume fraction of not more than 0.12 are recommended for further research. This research was funded under the research project No. 18-48-243014 by the Russian Foundation for Basic Research, the Government of the Krasnoyarsk Territory, as well as the Regional Foundation for Support of Research and Development Work. © 2019, "Ore and Metals" Publishing house. All rights reserved.

Ссылки на полный текст

Издание

Журнал: Tsvetnye Metally

Выпуск журнала: Vol. 2019, Is. 9

Номера страниц: 42-49

ISSN журнала: 03722929

Издатель: "Ore and Metals" Publishing house

Авторы

  • Yasinsky A.S. (School of non-ferrous metals and material science, Siberian federal university, Krasnoyarsk, Russian Federation)
  • Padamata S.K. (School of non-ferrous metals and material science, Siberian federal university, Krasnoyarsk, Russian Federation)
  • Polyakov P.V. (School of non-ferrous metals and material science, Siberian federal university, Krasnoyarsk, Russian Federation)
  • Vinogradov O.O. (School of non-ferrous metals and material science, Siberian federal university, Krasnoyarsk, Russian Federation)

Вхождение в базы данных

Информация о публикациях загружается с сайта службы поддержки публикационной активности СФУ. Сообщите, если заметили неточности.

Вы можете отметить интересные фрагменты текста, которые будут доступны по уникальной ссылке в адресной строке браузера.