Influence of the oxygen concentration on the formation of crystalline phases of TiO2 during the low-pressure arc-discharge plasma synthesis

Тип публикации: статья из журнала

Год издания: 2016

Идентификатор DOI: 10.1134/S1063784216020262

Аннотация: The synthesis of titanium dioxide (TiO2) nanoparticles with different percentage of anatase and rutile phases is investigated. The synthesis is performed by controlling the oxygen percentage in the gas mixture in the plasmachemical evaporation-condensation process employing a low-pressure arc discharge. In all our experiments, the pressure in the plasmachemical reactor and the average size of particles remain constant and are 60 Pa and 6 nm, respectively. The crystal structure of synthesized TiO2 is studied using X-ray diffraction; the morphology of the particles is analyzed employing transmission electron microscopy. Using X-ray phase analysis, it is established that the concentration of the TiO2 anatase phase decreases upon a decrease in the oxygen concentration in the gas mixture. It is shown that the TiO2 anatase phase is more efficient for photocatalytic decomposition of methylene blue than the rutile phase.

Ссылки на полный текст

Издание

Журнал: TECHNICAL PHYSICS

Выпуск журнала: Vol. 61, Is. 2

Номера страниц: 260-264

ISSN журнала: 10637842

Место издания: NEW YORK

Издатель: MAIK NAUKA/INTERPERIODICA/SPRINGER

Авторы

  • Ushakov A.V. (Reshetnev Siberian State Aerospace University)
  • Karpov I.V. (Reshetnev Siberian State Aerospace University)
  • Lepeshev A.A. (Krasnoyarsk Scientific Center,Siberian Branch,Russian Academy of Sciences)

Вхождение в базы данных

Информация о публикациях загружается с сайта службы поддержки публикационной активности СФУ. Сообщите, если заметили неточности.

Вы можете отметить интересные фрагменты текста, которые будут доступны по уникальной ссылке в адресной строке браузера.