High-temperature oxidation of nickel-based alloys and estimation of the adhesion strength of resulting oxide layers

Тип публикации: статья из журнала

Год издания: 2011

Идентификатор DOI: 10.1134/S2070205111030051

Ключевые слова: Film microstructures, High-temperature exposure, Isothermal oxidations, Nickel based alloy, Oxide layer, Spinel layers, Sulfur contents, TiO, Work of adhesion, Adhesion, Bond strength (materials), Iron alloys, Oxidation, Sulfur, Titanium dioxide, X ray diffraction, Oxide films

Аннотация: The kinetics of isothermal oxidation (1100A degrees C) of commercial nickel-based alloys with different content of sulfur (0.22-3.2 wt ppm) is studied. The adhesion strength in a metal/oxide system is estimated as a function of sulfur content and duration of high-temperature exposure. The scratch-test technique is proposed to quantitatively estimate the work of adhesion of resulting oxide films. It is found that the film microstructure is composed of an inner alpha-Al(2)O(3) layer and an outer NiAl(2)O(4) spinel layer, which are separated by discrete inclusions of TiO(2). Residual stresses in the oxide film are experimentally determined by X-ray diffraction.

Ссылки на полный текст

Издание

Журнал: PROTECTION OF METALS AND PHYSICAL CHEMISTRY OF SURFACES

Выпуск журнала: Vol. 47, Is. 3

Номера страниц: 347-353

ISSN журнала: 20702051

Место издания: NEW YORK

Издатель: MAIK NAUKA/INTERPERIODICA/SPRINGER

Авторы

  • Fedorova E.N. (Institute Carnot,CIRIMAT,ENSIACET)
  • Khudonogov S.A. (Siberian Federal University)
  • Monceau D. (Institute Carnot,CIRIMAT,ENSIACET)
  • Oquab D. (Institute Carnot,CIRIMAT,ENSIACET)

Вхождение в базы данных

Информация о публикациях загружается с сайта службы поддержки публикационной активности СФУ. Сообщите, если заметили неточности.

Вы можете отметить интересные фрагменты текста, которые будут доступны по уникальной ссылке в адресной строке браузера.