Quantification of growth kinetics and adherence of oxide scales formed on Ni-based superalloys at high temperature

Тип публикации: статья из журнала

Год издания: 2010

Идентификатор DOI: 10.1016/j.corsci.2010.08.013

Ключевые слова: Nickel, Superalloys, Oxidation, Interfaces, SEM, A. Nickel, A. Superalloys, B. SEM, C. Interfaces, C. Oxidation, A. Nickel, A. Superalloys, C. Interfaces, C. Oxidation, SEM, Adhesion, Growth kinetics, Oxidation, Scale (deposits), Sulfur, Superalloys

Аннотация: Cyclic and isothermal oxidation behaviors of first and fourth-generation superalloys AM1 and MCNG were investigated to evaluate the ability of the scratch test to quantify the adhesion of multi-layered oxide scales. Effects of sulfur content and of scale thickness were studied independently. Available models lead to large discrepancies in the calculated work of adhesion values with the evaluation of the residual stress being the largest source of error. Nevertheless, models can assess the effect of sulfur content and the scratch test can be used to correlate the long-term cyclic oxidation behavior and the adhesion of oxide scales. (C) 2010 Elsevier Ltd. All rights reserved.

Ссылки на полный текст

Издание

Журнал: CORROSION SCIENCE

Выпуск журнала: Vol. 52, Is. 12

Номера страниц: 3932-3942

ISSN журнала: 0010938X

Место издания: OXFORD

Издатель: PERGAMON-ELSEVIER SCIENCE LTD

Авторы

  • Fedorova E. (ENSIACET, Inst Carnot CIRIMAT, F-31030 Toulouse 4, France; Siberian Fed Univ, Polytech Inst, Krasnoyarsk 660074, Russia)
  • Monceau D. (ENSIACET, Inst Carnot CIRIMAT, F-31030 Toulouse 4, France)
  • Oquab D. (ENSIACET, Inst Carnot CIRIMAT, F-31030 Toulouse 4, France)

Вхождение в базы данных

Информация о публикациях загружается с сайта службы поддержки публикационной активности СФУ. Сообщите, если заметили неточности.

Вы можете отметить интересные фрагменты текста, которые будут доступны по уникальной ссылке в адресной строке браузера.