Nonstoichiometry of Bismuth Germanate and Bismuth Silicate with the Sillenite Structure

Тип публикации: статья из журнала

Год издания: 1998

Аннотация: Precision thermogravimetry and thermoelectric measurements showed that bismuth germanate Bi12GeO20 (BGO) and bismuth silicate Bi12SiO20 (BSO) have oxygen nonstoichiometry. It was shown that doubly charged anionic vacancies are the dominant type of defect over a wide range of temperatures. The concentration V0 ·· in crystals of the compounds in question was determined for temperatures from 823 to 1033 K and oxygen partial pressures from 1 to 10-3 Pa. The thermodynamic and kinetic characteristics of defect formation were calculated.

Ссылки на полный текст

Издание

Журнал: Russian Journal of Inorganic Chemistry

Выпуск журнала: Vol. 43, Is. 9

Номера страниц: 1313-1316

ISSN журнала: 00360236

Авторы

  • Shimanskii A.F. (Krasnoyarsk State Acad. Nonfer. M., Krasnoyarskii rabochii pr. 95, Krasnoyarsk, 660025, Russian Federation)

Вхождение в базы данных

Информация о публикациях загружается с сайта службы поддержки публикационной активности СФУ. Сообщите, если заметили неточности.

Вы можете отметить интересные фрагменты текста, которые будут доступны по уникальной ссылке в адресной строке браузера.