Low-field magnetization of ludwigites Co3O2BO3 and Co3-x Fe (x) O2BO3 (x a parts per thousand 0.14)

Тип публикации: статья из журнала

Год издания: 2009

Идентификатор DOI: 10.1134/S1063783409050138

Аннотация: Ludwigite single crystals of compositions Co3O2BO3 and Co3 - x Fe (x) O2BO3 (x a parts per thousand 0.14) have been synthesized. The crystal structure is investigated at room temperature, and the magnetization is studied in the temperature range T = 4.2-100 K in magnetic fields of up to 600 Oe. The orthorhombic symmetry is revealed, and the unit cell parameters are determined. A number of features are established for the temperature dependence of the magnetization. In unsubstituted Co3O2BO3, two magnetic transitions are found at T (C1) = 43 K and T (C2) = 15 K. At temperatures below 40 K, spin-glass state is revealed. Substitution of iron ions for cobalt ions leads to a noticeable shift in the magnetic transitions toward the high-temperature range: T (C1) = 83 K and T (C2) = 74 K. A ferromagnetic ordering of the P type is found in the Co3 - x Fe (x) O2BO3 (x a parts per thousand 0.14) compound.

Ссылки на полный текст

Издание

Журнал: PHYSICS OF THE SOLID STATE

Выпуск журнала: Vol. 51, Is. 5

Номера страниц: 966-969

ISSN журнала: 10637834

Место издания: NEW YORK

Издатель: MAIK NAUKA/INTERPERIODICA/SPRINGER

Авторы

  • Kazak N.V. (Kirensky Institute of Physics,Siberian Branch,Russian Academy of Sciences)
  • Rudenko V.V. (Kirensky Institute of Physics,Siberian Branch,Russian Academy of Sciences)
  • Vasil'Ev A.D. (Kirensky Institute of Physics,Siberian Branch,Russian Academy of Sciences)
  • Velikanov D.A. (Kirensky Institute of Physics,Siberian Branch,Russian Academy of Sciences)
  • Ovchinnikov S.G. (Kirensky Institute of Physics,Siberian Branch,Russian Academy of Sciences)
  • Ivanova N.B. (Siberian Federal University)

Вхождение в базы данных

Информация о публикациях загружается с сайта службы поддержки публикационной активности СФУ. Сообщите, если заметили неточности.

Вы можете отметить интересные фрагменты текста, которые будут доступны по уникальной ссылке в адресной строке браузера.