Сибирский федеральный университет

Тип публикации: статья из журнала

Год издания: 2020

Идентификатор DOI: 10.17516/1998-2836-0192

Ключевые слова: composite material, high-calcium fly ash, superplasticizer, hardening accelerator, retarder

Аннотация: Composite materials (CM) were obtained on the basis of fine-dispersed high-calcium fly ash (HCFA), selected from the 4th field of electrostatic precipitators of Krasnoyarsk TPP-2, with the addition of Melflux 5581F superplasticizer at the water: binder ratio W/B = 0.25. The influence of the concentration of superplasticizer in the range 0.06-0.6 wt. % on the strength properties of composite materials was studied. The effect of the addition of sodium sulfate as an accelerator of hydration hardening and additives-retarders of sodium phosphate, sodium tetraborate and citric acid, were studied. The optimal concentration of superplasticizer was established (0.3 wt. %). It was determined that sodium sulfate helps to improve the strength of CM, and the addition of sodium tetraborate and citric acid can effectively regulate the setting time. Composite materials (CM) were obtained on the basis of fine- dispersed high-calcium fly ash (HCFA), selected from the 4th field of electrostatic precipitators of Krasnoyarsk TPP-2, with the addition of Melflux 5581F superplasticizer at the water: binder ratio W/B = 0.25. The influence of the concentration of superplasticizer in the range 0.06-0.6 wt. % on the strength properties of composite materials was studied. The effect of the addition of sodium sulfate as an accelerator of hydration hardening and additives-retarders of sodium phosphate, sodium tetraborate and citric acid, were studied. The optimal concentration of superplasticizer was established (0.3 wt. %). It was determined that sodium sulfate helps to improve the strength of CM, and the addition of sodium tetraborate and citric acid can effectively regulate the setting time. © Siberian Federal University. All rights reserved

Журнал: JOURNAL OF SIBERIAN FEDERAL UNIVERSITY-CHEMISTRY

Выпуск журнала: Vol. 13, Is. 3

Номера страниц: 395-407

ISSN журнала: 19982836

Место издания: KRASNOYARSK

Издатель: SIBERIAN FEDERAL UNIV

• Sharonova Olga M. (FRC Krasnoyarsk Sci Ctr SB RAS, Inst Chem & Chem Technol SB RAS, Krasnoyarsk, Russia)
• Kirilets Valerii M. (FRC Krasnoyarsk Sci Ctr SB RAS, Inst Chem & Chem Technol SB RAS, Krasnoyarsk, Russia)
• Solovyov Leonid A. (FRC Krasnoyarsk Sci Ctr SB RAS, Inst Chem & Chem Technol SB RAS, Krasnoyarsk, Russia)
• Anshits Alexander G. (FRC Krasnoyarsk Sci Ctr SB RAS, Inst Chem & Chem Technol SB RAS, Krasnoyarsk, Russia; Siberian Fed Univ, Krasnoyarsk, Russia)

• Web of Science Core Collection
• Scopus
• Ядро РИНЦ (eLIBRARY.RU)
• Список ВАК