Nonstoichiometry and mass transport in bismuth titanate with sillenite structure

Тип публикации: статья из журнала

Год издания: 1996

Аннотация: Disordering processes in bismuth titanate with the sillenite-type structure were studied by thermogravimetry. It was shown that, in the range of oxygen partial pressures from 10(5) to 0.26 Pa, the off-stoichiometry in Bi12TiO20 is primarily due to doubly ionized oxygen vacancies. At lower values of rho(o2), defects on cation sites prevail. The experimental results were used to evaluate the thermodynamic and kinetic parameters of defect formation in the oxygen sublattice.

Ссылки на полный текст

Издание

Журнал: INORGANIC MATERIALS

Выпуск журнала: Vol. 32, Is. 3

Номера страниц: 305-307

ISSN журнала: 00201685

Место издания: NEW YORK

Издатель: MAIK NAUKA/INTERPERIODICA

Авторы

  • Shimanskii A.F. (Krasnoyarsk State Acad. Nonfer. M.)
  • Gritsenko D.A. (Krasnoyarsk State Acad. Nonfer. M.)
  • Derikova M.G. (Krasnoyarsk State Acad. Nonfer. M.)
  • Shvaiko-Shvaikovskii V.E. (Grebenshchikov Inst. Silicate Chem.,Russian Academy of Sciences)
  • Kargin Yu.F. (Kurnakov Inst. Gen. and Inorg. Chem.,Russian Academy of Sciences)

Вхождение в базы данных

Информация о публикациях загружается с сайта службы поддержки публикационной активности СФУ. Сообщите, если заметили неточности.

Вы можете отметить интересные фрагменты текста, которые будут доступны по уникальной ссылке в адресной строке браузера.