Conductivity study of Co3O2BO3 and Co 3-xFexO2BO3 oxyborates

Тип публикации: статья из журнала (материалы конференций, опубликованные в журналах)

Год издания: 2009

Идентификатор DOI: 10.4028/www.scientific.net/SSP.152-153.104

Ключевые слова: Doped cobaltite, Electrical conductivity, Ludwigite, Variable-range hopping, Crystal structure, Electric conductivity, Magnetic materials, Single crystals, Magnetism, Electrical resistivity, Experimental data, Mott variable-range hopping, Oxyborates, Temperature regions, Variable range hopping, Cobalt

Аннотация: Single crystals of cobalt oxyborates Co3O2BO 3 and Co3-xFexO2BO3 were synthesized. The crystal structure and electric properties were investigated. The difference in the electrical resistivity behaviors was found. For parent Co3O2BO3 nor simple activation law, nor Mott variable range hopping (VRH) are acquirable to describe the experimental data in wide temperature region. In contrast for Co3-xFex O 2BO3 Mott's variable-range hopping conductivity clearly dominates.

Ссылки на полный текст

Издание

Журнал: (20 June 2008 through 25 June 2008, Moscow

Выпуск журнала: Vol. 152-153

Номера страниц: 104-107

Вхождение в базы данных

Информация о публикациях загружается с сайта службы поддержки публикационной активности СФУ. Сообщите, если заметили неточности.

Вы можете отметить интересные фрагменты текста, которые будут доступны по уникальной ссылке в адресной строке браузера.