Special features of metallurgical processes in plasma welding of chromium bronze

Тип публикации: статья из журнала

Год издания: 2012

Идентификатор DOI: 10.1080/09507116.2011.592710

Ключевые слова: alloying, mechanical properties, plasma arc welding, void and crack formation, Chromium-bronze, Hot cracks, Metallurgical process, Weld pool, Alloying, Bronze, Chromium, Crack initiation, Cracks, Electric welding, Mechanical properties, Plasma welding, Metallurgy

Аннотация: The metallurgical processes taking place in the weld pool in plasma welding of chromium bronze are investigated. The reasons for the formation of defects, hot cracks, and pores are determined, and measures that should be taken to prevent the formation of these defects are indicated. © 2012 Taylor and Francis Group, LLC.

Ссылки на полный текст

Издание

Журнал: Welding International

Выпуск журнала: Vol. 26, Is. 1

Номера страниц: 36-39

ISSN журнала: 09507116

Авторы

  • Novosel'tsev Y.G. (Polytechnical Institute of the Siberian Federal University, Krasnoyarsk, Russian Federation)
  • Tuf S.M. (Polytechnical Institute of the Siberian Federal University, Krasnoyarsk, Russian Federation)