Synthesis and magnetic properties of polycrystalline films of CoxFeyCr3-x-yO4 and Cr2O3/CoFe2O4 multiferroics

Тип публикации: статья из журнала

Год издания: 2014

Идентификатор DOI: 10.1134/S1063785014080136

Аннотация: Magnetic properties of first obtained polycrystalline films of FeCr2O4, CoCr2O4, and CoFe0.5Cr1.5O4 multiferroics and films of a Cr2O3/CoFe2O4 composite multiferroic have been studied. In particular, magnetization curves and temperature dependences of the magnetic moment of the samples were measured in the temperature range 4.2-300 K in fields of up to 10 kOe. It was shown that the Curie point of a multiferroic depends on its cation composition. It was found that an exchange bias of the hysteresis loop exists in films of the Cr2O3/CoFe2O4 composite multiferroic at temperatures below the N,el point of Cr2O3 (330 K).

Ссылки на полный текст

Издание

Журнал: TECHNICAL PHYSICS LETTERS

Выпуск журнала: Vol. 40, Is. 8

Номера страниц: 632-635

ISSN журнала: 10637850

Место издания: NEW YORK

Издатель: MAIK NAUKA/INTERPERIODICA/SPRINGER

Авторы

  • Polyakova K.P. (Siberian Federal University; Kirensky Institute of Physics, Siberian Branch, Russian Academy of Sciences)
  • Polyakov V.V. (Siberian Federal University; Kirensky Institute of Physics, Siberian Branch, Russian Academy of Sciences)
  • Velikanov D.A. (Siberian Federal University; Kirensky Institute of Physics, Siberian Branch, Russian Academy of Sciences)
  • Yurkin G.Y. (Siberian Federal University; Kirensky Institute of Physics, Siberian Branch, Russian Academy of Sciences)
  • Patrin G.S. (Siberian Federal University; Kirensky Institute of Physics, Siberian Branch, Russian Academy of Sciences)

Вхождение в базы данных

Информация о публикациях загружается с сайта службы поддержки публикационной активности СФУ. Сообщите, если заметили неточности.

Вы можете отметить интересные фрагменты текста, которые будут доступны по уникальной ссылке в адресной строке браузера.