Cryptocrystalline graphite chemical-mechanical preparation for subsequent processing stages

Тип публикации: статья из журнала

Год издания: 2016

Идентификатор DOI: 10.17580/or.2016.02.03

Ключевые слова: Antistick coating for iron casting, Chemically-mechanically activated graphite, Cryptocrystalline graphite, Differential thermal analysis (DTA), High-temperature X-ray phase analysis, X-ray diffractometer XRD-7000

Аннотация: A combined effect of chemical treatment and mechanical activation upon cryptocrystalline graphite condition was studied. Chemical-mechanical preparation was accomplished by means of sulfuric acid in the presence of potassium bichromate with subsequent activation in planetary centrifugal mill AGO-2 in optimal regimes. By means of optical and scanning electron microscopy, differential thermal analysis and X-ray phase analysis, it was established that consecutive chemical and mechanical treatment of natural cryptocrystalline graphite leads to liberation of graphite intergrowths with impurity minerals, permitting to decrease impurities content in its composition, also providing for decrease in particle average size and increase in nano-size fractions content. Removal of sulfur-containing compounds from graphite composition will hamper oxidation reactions of iron sulfur-containing compounds during crude iron casting into molds, preventing formation of sulfide-containing lowmelting phases in surface layer of antistick coating in cast iron-coating interface, contributing to antistick coating unwettability with molten iron and significantly decreasing burning-on formation on castings.

Ссылки на полный текст

Издание

Журнал: Obogashchenie Rud

Выпуск журнала: Is. 2

Номера страниц: 14-19

ISSN журнала: 02023776

Авторы

Вхождение в базы данных

Информация о публикациях загружается с сайта службы поддержки публикационной активности СФУ. Сообщите, если заметили неточности.

Вы можете отметить интересные фрагменты текста, которые будут доступны по уникальной ссылке в адресной строке браузера.