Synthesis and study of the magnetic characteristics of nanocrystalline cobalt films

Тип публикации: статья из журнала

Год издания: 2008

Идентификатор DOI: 10.1134/S1063783408040136

Аннотация: The effect of various technological factors on the main magnetic characteristics of nanocrystalline cobalt films obtained by chemical deposition is studied. The effective saturation magnetization, uniaxial anisotropy, coercive force, and other characteristics of local spots of films were measured using a scanning FMR spectrometer over the decimeter wavelength range. A technique for preparing substrates is developed, and the optimum technological conditions of thin-film synthesis are found making it possible to significantly decrease magnetic inhomogeneities across the area and thickness of samples. It is shown that one can significantly decrease the FMR linewidth and increase the magnetic permeability of films in a given microwave frequency range.

Ссылки на полный текст

Издание

Журнал: PHYSICS OF THE SOLID STATE

Выпуск журнала: Vol. 50, Is. 4

Номера страниц: 676-683

ISSN журнала: 10637834

Место издания: NEW YORK

Издатель: MAIK NAUKA/INTERPERIODICA/SPRINGER

Авторы

  • Belyaev B.A. (Kirensky Institute of Physics,Siberian Branch,Russian Academy of Sciences)
  • Kiparisov S.Ya. (Kirensky Institute of Physics,Siberian Branch,Russian Academy of Sciences)
  • Skomorokhov G.V. (Kirensky Institute of Physics,Siberian Branch,Russian Academy of Sciences)
  • Izotov A.V. (Siberian Federal University)

Вхождение в базы данных

Информация о публикациях загружается с сайта службы поддержки публикационной активности СФУ. Сообщите, если заметили неточности.

Вы можете отметить интересные фрагменты текста, которые будут доступны по уникальной ссылке в адресной строке браузера.